粒度不均匀铬矿石取样代表性的研究
A Study on the Representativeness of Sampling for Non-uniform Particle Size Chrome Ore
-
摘要: 以一批进口土耳其铬矿石为例,对所取的40个样品进行0~10 mm、10~50 mm、50~150 mm、150~250 mm及大于250 mm五个区间的粒度筛分,分析粒度不均匀的铬矿石在各粒度区间内组分含量和所占质量百分比的差异情况。根据分析结果对40个样品在50~150 mm区间内的质量百分比与样品总组分含量进行相关性分析,结果表明: 两者的相关系数为0.466,相关系数的显著性概率为0.002,小于0.01,说明在50~150 mm粒度区间内矿石的质量百分比与样品的总含量的相关性是高度显著的,提出为了提高粒度不均匀的铬矿石取样代表性,应首先保证在所含矿石质量百分比与总组分含量相关性最大的粒度区间内(50~150 mm),所取矿石样品与实际货物中矿石的质量百分比相一致。Abstract: Forty samples of imported Turkish chrome ore were classified into five size groups (0-10 mm, 10-50 mm, 50-150 mm, 150-250 mm and greater than 250 mm) in which the difference of constituent contents and weight proportions were studied. The relevance of weight proportions in the 50-150 mm particles and constituent contents of the 40 samples was studied. The results show a correlation coefficient of 0.466 and a significance probability of 0.002, which indicates a highly significant correlation between them. Therefore, in order to improve the representativeness of sampling, the weight proportions in the 50-150 mm particle group should be correlated between the sampling ore samples and the actual cargo.
-
Keywords:
- chrome /
- ore /
- non-uniform /
- particle
-
-
张建,王登红,付平.中国铬矿资源形势及其找矿方向[J].西北地质,2009,42(3): 69-76. 谷松海,宋义,郭芬.X射线荧光光谱法同时测定铬矿中主次成分[J].冶金分析,2008,28(4): 16-19. 胡德新,马德起,苏明跃,王虹,姚传刚.微波溶样-自动电位滴定法测定铬矿石中三氧化二铬[J].岩矿测试,2011,30(1): 83-86. ISO 6154—1989, Chromium Ores—Preparation of Samples [S]. ISO 6154—1989, Chromium Ores—Preparation of Samples [S].
廖立兵,李国武,蔡元峰,黄俊杰.粉晶X射线衍射在矿物岩石学研究中的应用[J].物理,2007,36(6): 460-464. 王小虎.岩石断裂的研究现状浅析[J].四川地质学报, 2007,27(2): 77-80. 冯涛,谢学斌.岩爆岩石断裂机理的电镜分析[J].中南工业大学学报,1999,30(1): 14-17. 李先纬,兰勇瑞,邹俊兴.岩石断口分析[J].中国矿业学院学报,1983(1): 15. 高峰,谢和平,赵鹏.岩石块度分布的分形性质及细观结构效应[J].岩石力学与工程学报,1994,13(3): 240-246. 罗英婷,杨钰娟.SPSS统计分析从基础到实践[M].北京: 电子工业出版社,2009: 195-199.
计量
- 文章访问数: 1527
- HTML全文浏览量: 2
- PDF下载量: 1447
下载:
京公网安备 11010202008159号